PP 7033E3 EXXONMOBIL SINGAPORE

119

Form：Granules | Grade：Injection grade

Properties:

Block copolymerHigh mobilityHigh rigidityHigh impact resistance

Typical Applications:

Plastic barrelPlastic boxToyIndustrial containersShellLoading boxBarrelRigid packageConsumer product application fieldIndustrial applicationscontainer

Supplier(1)

Product Description

Certificates(3)

Datasheet

Product Description

Typical Applications:	Plastic barrel \| Plastic box \| Toy \| Industrial containers \| Shell \| Loading box \| Barrel \| Rigid package \| Consumer product application field \| Industrial applications \| container
Properties:	Block copolymer \| High mobility \| High rigidity \| High impact resistance

Certificates

TDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	-29°C,3.18mm	ASTM D5420	28.1	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
	Impact strength of cantilever beam gap	-18°C	ISO 180/1A	5.7	kJ/m²
		Impact strength of cantilever beam gap	-40°C	ISO 180/1A	4.0	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256A	280	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14	kJ/m²
	Charpy Notched Impact Strength	0°C	ISO 179/1eA	6.7	kJ/m²
		Charpy Notched Impact Strength	-20°C	ISO 179/1eA	5.4	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.3	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	--6	ISO 178	1190	Mpa
	Bending modulus	1%Secant5	ASTM D790B	1280	Mpa
	Bending modulus	Bending modulus	1%Secant4	ASTM D790A	1140	Mpa
elongation	Yield	ISO 527-2/50	5.6	%
elongation	elongation	Yield3	ASTM D638	6.5	%
tensile strength	Yield	ISO 527-2/50	23.1	Mpa
tensile strength	tensile strength	Yield3	ASTM D638	23.9	Mpa
Tensile modulus		ISO 527-2/1	1290	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	50.9	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTM D648	114	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	85.3	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	90.2	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	8.0	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	89

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.