PP PP TM 40-1 Poly Plastic
0
- Properties:FillerPolyPlasticRussian PolyPlastic
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.24 g/cm³ | ||
| melt mass-flow rate | 2.6 g/10min | ||
| Shrinkage rate | 0.40to0.60 % | ||
| density | 1.24 g/cm³ | ||
| melt mass-flow rate | 2.6 g/10min | ||
| Shrinkage rate | 0.40to0.60 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | 3700 MPa | ||
| bending strength | 45.0 MPa | ||
| tensile strength | Yield | 30.0 MPa | |
| Tensile strain | Break | 37 % | |
| tensile strength | Yield | 30.0 MPa | |
| Tensile strain | Break | 37 % | |
| Flexural modulus | 3700 MPa | ||
| bending strength | 45.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | 6.0 kJ/m² | ||
| 20 kJ/m² | |||
| Charpy Notched Impact Strength | 3.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | 6.0 kJ/m² | ||
| 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | 1E+15 ohms·cm | ||
| 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | 125 °C | ||
| 75.0 °C | |||
| Melting Temperature | 164 °C | ||
| 6E-06 cm/cm/°C | |||
| 125 °C | |||
| 75.0 °C | |||
| Melting Temperature | 164 °C | ||
| 6E-06 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.