Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.70 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.67 % |
| Shrinkage rate | | ISO294-4 | 0.21 % |
| Shrinkage rate | | ISO2577 | 0.34 % |
| Shrinkage rate | | ISO2577 | 0.10 % |
| Water absorption rate | | ISO62 | 7.8 % |
| Water absorption rate | | ISO62 | 2.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 190 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| Extreme Oxygen Index 9 | | ISO4589-2 | 23 % |
| BurningBehavior10 | | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA6/66,GHR,14-060,GF15 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 35 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 40 kJ/m² |
| | ISO180/1U | 20 kJ/m² |
| | ISO180/1U | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 117 Mpa |
| Tensile stress | | ISO527-2/5 | 120 Mpa |
| elongation | | ASTMD638 | 3.0 % |
| Tensile strain | | ISO527-2/5 | 3.0 % |
| Flexural modulus | | ASTMD790 | 5700 Mpa |
| Flexural modulus | | ISO178/A | 5700 Mpa |
| bending strength | | ASTMD790 | 185 Mpa |
| Bending stress | | ISO178/A | -- Mpa |
| Bending stress | | ISO178 | 185 Mpa |
| Bending stress | | | 4.0 % |
| Tensile modulus | | ASTMD638 | 6310 Mpa |
| Tensile modulus | | ISO527-2/1 | 6300 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| | ISO6603-2 | 1.50 J |
| | ISO6603-2 | 2.00 J |
| | ISO6603-2 | 505 N |
| | ISO6603-2 | 560 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 30 KV/mm |
| | IEC60250 | 4.10 |
| | IEC60250 | 3.70 |
| Dissipation Factor | | IEC60250 | 8E-03 |
| Dissipation Factor | | IEC60250 | 0.018 |
| CTI | | IEC60112 | 375 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 3E-05 cm/cm/°C |
| | ISO11359-2 | 8E-05 cm/cm/°C |
| | ISO75-2/B | 210 °C |
| | ISO75-2/A | 180 °C |
| | ISO75-2/C | 55.0 °C |
| vicat | | ISO306/B50 | 200 °C |
| vicat | | ISO306/B120 | 200 °C |
| Melting temperature 5 | | ISO11357-3 | 218 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.