Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.20 g/cm³ |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO489 | 1.5850 |
| transmissivity | | DIN5036 | 86.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | >280 °C |
| SheetTemperature-Forming | | | 180到210 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 60.0 MPa |
| Tensile modulus | | ISO527-2 | 2200 MPa |
| Tensile strain | Break | ISO527-2 | 80 % |
| Bending stress | | ISO178 | >95.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | >10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | DIN53482 | 1E+15 ohms |
| Volume resistivity | | DIN53482 | 1E+15 ohms·cm |
| dielectric strength | | DIN53481 | >30 kV/mm |
| dielectric constant | | DIN53483 | 3.00 |
| Dissipation Factor | | DIN53483 | 8E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| maximum service temperature | | | 115 °C |
| maximum service temperature | | | 130 °C |
| vicat | | ISO306/B50 | 145 °C |
| | DIN53328 | 6.5E-05 cm/cm/°C |
| specific heat | | | 1170 J/kg/°C |
| thermal conductivity | | DIN52612 | 0.20 W/m/K |
| | ISO75-2 | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.