Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.18 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 2.2 g/10min |
| Shrinkage rate | | | 0.40to0.70 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 98 |
| ball-indentation hardness | | ISO 2039-1 | 185 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.490 |
| transmissivity | | ASTM D1003 | 92.0 % |
| Haze ratio | | ASTM D1003 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 83.0 MPa |
| Tensile strain | Break | ISO 527-2 | 5.0 % |
| Flexural modulus | | ISO 178 | 3200 MPa |
| bending strength | | ISO 178 | 115 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 2.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTME831 | 7.1E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/B | 105 °C |
| Heat distortion temperature | | ISO 75-2/A | 102 °C |
| vicat | | ISO 306/A | 117 °C |
| vicat | | ISO 306/B | 109 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.