Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.35到0.55 -- |
| Water absorption rate | | % | 1.0 -- |
| HeatStability | | °C | 100到110 -- |
| density | | g/cm³ | 1.32 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 122 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 7000 4500 |
| tensile strength | | MPa | 135 85.0 |
| elongation | | % | 3.5 5.5 |
| Flexural modulus | | MPa | 6500 4000 |
| bending strength | | MPa | 210 120 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 9.0 15 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 22 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 195 -- |
| | °C | 180 -- |
| melting temperature | | °C | 214到220 -- |
| | cm/cm/°C | 3E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare