PC/ABS FR3000 BK COVESTRO THAILAND

Form：Granules | Grade：Injection grade

Properties:

Flame retardantUV resistanceHigh mobility

Typical Applications:

Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesAutomotive sector

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Household appliances \| Household appliances \| Automotive sector
Properties:	Flame retardant \| UV resistance \| High mobility

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180/A	35	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/A	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	5VA
	UL flame retardant rating	2.0mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1	2700	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	60.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	45.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	3.5	%
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	>40	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	7.6E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	97.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	95.0	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	82.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	92.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD:240°C,3.00mm	ISO 2577	0.50-0.70	%
Shrinkage rate	Shrinkage rate	TD:240°C,3.00mm	ISO 2577	0.50-0.70	%
Melt Volume Flow Rate (MVR)	240°C/5.0kg	ISO 1133	24.0	cm3/10min
MeltViscosity	260°C	ISO 11443-A	160	Pa·s
density	23°C	ISO 1183	1.18	g/cm³
Water absorption rate	Saturation,23°C	ISO 62	0.50	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2
Dissipation factor	23°C,1MHz	IEC 60250	6E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	5E-03
Relative permittivity	23°C,1MHz	IEC 60250	3.10
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.20
Dielectric strength	23°C,1.00mm	IEC 60243-1	35	KV/mm
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.