Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.02 g/cm³ |
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| Shrinkage rate | | | 0.20到0.80 % |
| Water absorption rate | | ISO62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 55 |
| | ISO868 | 71 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ISO3537 | 90.0 % |
| Haze ratio | | ISO3537 | 0.50 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2/5 | 27.0 MPa |
| Tensile strain | Break | ISO527-2/5 | 200 % |
| Flexural modulus | | ISO178 | 1200 MPa |
| Bending stress | | ISO178 | 37.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Complete Break | ISO179 | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Complete Break | ISO179 | 100 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 57.0 °C |
| vicat | | ISO306/A50 | 82.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.