Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.912 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 33 |
| Haze ratio | | ASTM D1003 | 1.7 % |
| transparency | | ASTM D1746 | 97 |
| gloss | | ASTM D2457 | 67 |
| Haze ratio | | ASTM D1003 | 8 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 1.0 g/10min |
| density | | ASTM D792 | 0.9120 g/cm3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation at break | | ASTM D882 | 464 % |
| Tensile modulus | | ASTM D882 | 128 MPa |
| Puncture Strength | | 陶氏企业测试 | 24 J/cm3 |
| tensile strength | | ASTM D882 | 10 MPa |
| tensile strength | | ASTM D882 | 49 MPa |
| film | Test Condition | Test Method | Test Result |
|---|
| Thin film puncture strength | | 内部方法 | 31.4 J/cm³ |
| Secant modulus | | ASTM D882 | 138 MPa |
| Secant modulus | | ASTM D882 | 141 MPa |
| tensile strength | | ASTM D882 | 10.1 MPa |
| tensile strength | | ASTM D882 | 9.03 MPa |
| tensile strength | | ASTM D882 | 38.5 MPa |
| tensile strength | | ASTM D882 | 34.4 MPa |
| elongation | | ASTM D882 | 520 % |
| elongation | | ASTM D882 | 710 % |
| Dart impact | | ASTM D1709B | 870 g |
| Elmendorf tear strength | | ASTM D1922 | 370 g |
| Elmendorf tear strength | | ASTM D1922 | 590 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | 内部方法 | 123 °C |
| vicat | | ASTM D1525 | 92.8 °C |
| vicat | | ASTM D1525 | 93 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.