Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.53 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.25 % |
| Shrinkage rate | | ISO 294-4 | 0.15 % |
| Water absorption rate | | ISO 62 | >0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 89 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Flowability | | 内部方法 | 145 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 165 MPa |
| Tensile strain | Break | ISO 527-2 | 1.1 % |
| Flexural modulus | | ISO 178 | 19300 MPa |
| bending strength | | ISO 178 | 250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 8.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+02 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.7E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | 274 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.