PA6 1013NW8 UCHA THAILAND

104

Form：Granules | Grade：Injection grade

Properties:

Low viscosityFast forming cycle

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Low viscosity | Fast forming cycle

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	5.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.66mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	110	Mpa
Bending modulus		ISO 178	2700	Mpa
Tensile strain	Break	ISO 527-2	20	%
tensile strength	Yield	ISO 527-2	85.0	Mpa
Tensile modulus		ISO 527-2	3200	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	175	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	Internal Method	2.5	%
Shrinkage rate	MD	Internal Method	1.2	%
Shrinkage rate	Shrinkage rate	TD	Internal Method	1.3	%
density		ISO 1183	1.14	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Arc resistance		ASTM D495	119	sec
Relative permittivity		IEC 60250	3.50
Dielectric strength		IEC 60243-1	20	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.