Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.14 g/cm³ |
Shrinkage rate | | 内部方法 | 1.1to1.7 % |
Water absorption rate | | ISO 62 | 1.2 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-2 |
Burning wire flammability index | | IEC 60695-2-12 | 750 °C |
Limiting Oxygen Index | | ISO 4589-2 | 27 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 2800 MPa |
tensile strength | Yield | ISO 527-2 | 75.0 MPa |
Flexural modulus | | ISO 178 | 2900 MPa |
bending strength | | ISO 178 | 95.0 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179 | 13 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179 | NoBreak |
Electrical performance | Test Condition | Test Method | Test Result |
---|
dielectric strength | | IEC 60243-1 | 18 kV/mm |
relative permittivity | | IEC 60250 | 3.80 |
Dissipation Factor | | IEC 60250 | 0.020 |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
Surface Resistivity | | IEC 60093 | 1E+14 ohms |
Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/B | 225 °C |
Heat distortion temperature | | ISO 75-2/A | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.