Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ISO1183 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238,ISO1133 | 17 g/10min |
| Shrinkage rate | | ASTMD955 | 0.50到0.70 % |
| Water absorption rate | | ASTMD570 | 0.23 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 75 |
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 85.0 % |
| refractive index | | ASTMD542,ISO489 | 1.586 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638,ISO527-2 | 2300 MPa |
| tensile strength | Yield | ASTMD638,ISO527-2 | 63.0 MPa |
| tensile strength | Break | ASTMD638,ISO527-2 | 68.0 MPa |
| elongation | Break | ASTMD638,ISO527-2 | 100 % |
| Flexural modulus | | ASTMD790,ISO178 | 2350 MPa |
| bending strength | | ASTMD790,ISO178 | 93.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 780 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 29 kV/mm |
| dielectric constant | | ASTMD150 | 2.91 |
| dielectric constant | | ASTMD150 | 2.85 |
| Dissipation Factor | | ASTMD150 | 6.6E-04 |
| Dissipation Factor | | ASTMD150 | 9.2E-03 |
| arc resistance | | ASTMD495 | 110 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648,ISO75-2/A | 132 °C |
| | ASTMD696 | 6.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.