ASA/PC GELOY™ HRA222F-GY6G053 SABIC INNOVATIVE NANSHA
705
- Properties:High temperature resistanThermal stability
- Usages:Home appliance componentsLawn garden equipment
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 13.0 | cm3/10min |
| Shrinkage rate - Flow | 内部方法 | 0.40 到 0.60 | % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.60 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Outdoor applicability | UL 746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 3 | ASTM D638 | 2590 | Mpa |
| -- | ISO 527-2/1 | 2520 | Mpa | |
| tensile strength | 屈服 4 | ASTM D638 | 63.0 | Mpa |
| 屈服 5 | ASTM D638 | 59.0 | Mpa | |
| 屈服 | ISO 527-2/5 | 62.0 | Mpa | |
| 屈服 | ISO 527-2/50 | 60.0 | Mpa | |
| 断裂 5 | ASTM D638 | 66.0 | Mpa | |
| 断裂 4 | ASTM D638 | 56.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 51.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 45.0 | Mpa | |
| elongation | 屈服 5 | ASTM D638 | 4.2 | % |
| 屈服 4 | ASTM D638 | 4.3 | % | |
| 屈服 | ISO 527-2/5 | 4.3 | % | |
| 屈服 | ISO 527-2/50 | 4.4 | % | |
| 断裂 5 | ASTM D638 | > 100 | % | |
| 断裂 4 | ASTM D638 | > 100 | % | |
| 断裂 | ISO 527-2/5, ISO 527-2/50 | > 50 | % | |
| Bending modulus | ISO 178 | 2510 | Mpa | |
| Bending stress 6, | ISO 178 | 93.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 99.0 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 88.0 | °C | |
| vicat softening point | -- | ISO 306/A50 | 111 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 104 | °C | |
| Ball Pressure Test | 73 到 77°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | 流动 : -30 到 80°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C |
| 横向 : -30 到 80°C | ISO 11359-2 | 7.1E-5 | cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI | UL 746 | 90.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | ||
| Leakage Trace Index | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 200 到 230 | °C | ||
| Temperature in the middle of the barrel | 220 到 260 | °C | ||
| Temperature at the front of the material cylinder | 230 到 270 | °C | ||
| Spray nozzle temperature | 220 到 260 | °C | ||
| Processing (melt) temperature | 230 到 270 | °C | ||
| Mold temperature | 50 到 70 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.0 mm | UL 94 | V-0 | |
| Extreme Oxygen Index | ISO 4589-2 | 29 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.