HIPS POLYREX® PH-879
845
- Properties:High mobilityFlame retardant
- Usages:Wire and cable
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 10.0 (Cond.G)g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 7.0(1.28) kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 8.5(1.56) kg·cm/cm(J/M)ft·lb/in | ||
| Rockwell hardness | ASTM D785 | 75 | |
| Flexural modulus | ASTM D790/ISO 178 | 1.7(2.4) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 410(5820) kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D-256 | 7.0(1.28) kg.cm/cm(ft.lb/in) | |
| ASTM D-256 | 8.5(1.56) kg.cm/cm(ft.lb/in) | ||
| Flexural modulus | ASTM D-790 | 1.7(2.4) | |
| Shore hardness | ASTM D-785 | 75 L | |
| bending strength | ASTM D-790 | 410(5820) kg/cm | |
| elongation at break | ASTM D-638 | 45 % | |
| tensile strength | ASTM D-638 | 300(4260) kg/cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10.0 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 1/16"V-0 | |
| Heat distortion temperature | ASTM D648/ISO 75 | 80(176) ℃（℉） | |
| vicat | ASTM D1525/ISO R306 | 94(201) ℃（℉） | |
| Heat distortion temperature | ASTM D-648 | 80(176) ℃(°F) | |
| vicat | ASTM D-1525 | 94(201) ℃(°F) | |
| burning rate | File No E56070 UL&C-CL | 1/16"V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.