Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.49 g/cm³ |
| melt mass-flow rate | | ISO1133 | 20 g/10min |
| Shrinkage rate | | ISO294-4 | 0.80to1.1 % |
| Shrinkage rate | | ISO294-4 | 0.10to0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 9600 MPa |
| Tensile stress | | ISO527-2 | 140 MPa |
| Tensile strain | | ISO527-2 | 2.5 % |
| Flexural modulus | | ISO178 | 7700 MPa |
| Bending stress | | ISO178 | 200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 13 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 23 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 210 °C |
| | ISO75-2/A | 200 °C |
| melting temperature | | ISO11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.