Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.61到1.71 g/cm³ |
| | | 2.5到3.5 Pa·s |
| Curing Time | | | 16到24 hr |
| STORAGE STABILITY | | | 45到60 min |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:20 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 82到88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 6450到6550 MPa |
| Bending stress | | ISO178 | 55.0到65.0 MPa |
| compression stress | | ISO604 | 75.0到85.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 4.5到5.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 47.0到51.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.