Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 1.1 % |
| Shrinkage rate | | | 2.1 % |
| Water absorption rate | | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 72 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 70.0 Mpa |
| elongation | | ASTM D638 | 4.7 % |
| Flexural modulus | | ASTM D790 | 4400 Mpa |
| bending strength | | ASTM D790 | 106 Mpa |
| | | 0.19 |
| Wear amount | | | 0.500 10^-3 mm³/N·km |
| Wear amount | | | 0.00 10^-3 mm³/N·km |
| injection | Test Condition | Test Method | Test Result |
|---|
| Processing (melt) temperature | | | 185 到 215 °C |
| Temperature | | | 60 到 100 °C |
| Injection Pressure | | | 70.0 到 100 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D696 | 7.0E-5 cm/cm/°C |
| Heat Distortion | | ASTM D648 | 136 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.