ABS ABS M305 ELIX Polymers, S. L.

0

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
Melt volume flow rateISO 113312.0 cm³/10min
Shrinkage rateISO 294-40.50to0.80 %
Shrinkage rateISO 294-40.50to0.80 %
hardnessTest ConditionTest MethodTest Result
ball-indentation hardnessISO 2039-195.0 MPa
flammabilityTest ConditionTest MethodTest Result
burning rateISO 379550 mm/min
Burning wire flammability indexIEC 60695-2-12700 °C
Mechanical propertiesTest ConditionTest MethodTest Result
Flexural modulusISO 1782300 MPa
bending strengthISO 17868.0 MPa
Tensile strainISO 527-2/50>15 %
Tensile modulusISO 527-2/12300 MPa
tensile strength ISO 527-2/5045.0 MPa
Tensile strainISO 527-2/502.5 %
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact StrengthISO 179/1eA11 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA21 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU110 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU150 kJ/m²
Impact strength of cantilever beam gapISO 180/1A11 kJ/m²
Impact strength of cantilever beam gapISO 180/1A21 kJ/m²
Electrical performanceTest ConditionTest MethodTest Result
Dissipation FactorIEC 602505E-03
Dissipation FactorIEC 602508E-03
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
Surface ResistivityIEC 600931E+15 ohms
Volume resistivityIEC 600931E+15 ohms·cm
dielectric strengthIEC 60243-134 kV/mm
relative permittivityIEC 602503.10
relative permittivityIEC 602502.90
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureISO 75-2/B98.0 °C
Heat distortion temperatureISO 75-2/A94.0 °C
vicatISO 306/B5099.0 °C
Linear coefficient of thermal expansionISO 11359-29E-05 cm/cm/°C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.