PA6 VOLGAMID® G30 NC201 KUAZOT SHANGHAI
97
- Properties:Thermal stabilityDimensional stabilityHigh rigidity30% short fiber enhanceme
- Usages:Fitness equipmentAutomotive sector
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning residue | ISO 1172 | 30.1 | |
| Water absorption rate | ISO 62 | 1.9 % | |
| Shrinkage rate | ISO 294-4 | 0.10 | |
| ISO 294-4 | 0.50 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2239/2 | 117 | |
| tensile strength | ISO 527 | 169 Mpa | |
| elongation | ISO 527 | 2.7 % | |
| bending strength | ISO 178 | 240 Mpa | |
| Flexural modulus | ISO 178 | 7592 Mpa | |
| Impact strength of simply supported beam without notch | ISO 179 | 92.7 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179 | 14.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1012 Ω | |
| dielectric strength | IEC 60243 | 22 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75 | 208 °C | |
| melting temperature | ISO 3461 | 220 °C | |
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.