PC 2458 010110 COVESTRO GERMANY

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh mobility

Typical Applications:

Automotive ApplicationsLighting installationelectrical equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Lighting installation \| electrical equipment
Properties:	Flame retardant \| High mobility

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	2000μm	ISO 13468-2	89.0	%
	transmissivity	3000μm	ISO 13468-2	88.0	%
	transmissivity	transmissivity	4000μm	ISO 13468-2	87.0	%
turbidity	3000μm	ISO 14782	<0.80	%
Refractive index		ISO 489	1.586
transmissivity	1000μm	ISO 13468-2	89.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5100	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6000	N
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	55.0	J
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	14	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	65	kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	15	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	65	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	65.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	28	%
FlashIgnitionTemperature		ASTM D1929	480	°C
SelfIgnition		ASTM D1929	550	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,23°C	ISO 527-2/50	130	%
Tensile strain	Tensile strain	Yield,23°C	ISO 527-2/50	6.1	%
tensile strength	Break,23°C	ISO 527-2/50	70.0	Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2/50	65.0	Mpa
Tensile modulus	23°C	ISO 527-2/1	2400	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
Tensile creep modulus	1hr	ISO 899-1	2200	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1900	Mpa
Bending modulus	23°C	ISO 178	2350	Mpa
bending strength	3.5%Strain,23°C	ISO 178	73.0	Mpa
bending strength	bending strength	23°C	ISO 178	97.0	Mpa
Bending strain	23°C	ISO 178	7.1	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	138°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B120	146	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145	°C
Glass transition temperature		ISO 11357-2	146	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	139	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Shrinkage rate	MD:2.00mm3	ISO 294-4	0.65	%
	Shrinkage rate	TD:2.00mm3	ISO 294-4	0.70	%
		Shrinkage rate	MD	ISO 2577	0.50-0.70	%
		Shrinkage rate	Shrinkage rate	TD	ISO 2577	0.50-0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	19.0	cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	20	g/10min
Apparent density		ISO 60	0.66	g/cm³
density	23°C	ISO 1183	1.20	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	34	KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.00
Dissipation factor	23°C,100Hz	IEC 60250	5E-04
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	9E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	115	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.