Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 2.0 g/10min |
| other | Test Condition | Test Method | Test Result |
|---|
| notes | | | 薄膜级 |
| characteristic | | | 及佳的透明度.冲击强度和加工性。典型加工温度 模头:160-180℃ |
| purpose | | | 通用包装、农膜 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Additive content | | | 增滑剂与防粘剂 |
| melt mass-flow rate | | ASTM D-1238 | 2 g/10min |
| density | | ASTM D-1505 | 0.923 g/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 24.5 Mpa |
| elongation | | ASTM D638 | 800 % |
| Flexural modulus | | ASTM D747 | 270 Mpa |
| tensile strength | | ASTM D-638 | 250 kg/cm |
| elongation | | ASTM D-638 | 850 % |
| bending strength | | ASTM D-747 | 2400 kg/cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.923 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | | 123 ℃（℉） |
| melting temperature | | | 122 °C |
| melting temperature | | TPC法 | 123 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare