Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.33 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 57 |
| Haze ratio | | ASTM D1003A | 8.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Viscosity | | 内部方法 | 30 g |
| Re-blocking | | 内部方法 | 10 g |
| tear strength | | ISO 6383-2 | 35.0 kN/m |
| tear strength | | ISO 6383-2 | 40.0 kN/m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D4272 | 300 J/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | ASTM D1894 | 1.0 |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-3 | 11.0 Mpa |
| tensile strength | | ISO 527-3 | 27.0 Mpa |
| tensile strength | | ISO 527-3 | 22.0 Mpa |
| elongation | | ISO 527-3 | >200 % |
| elongation | | ISO 527-3 | >500 % |
| Tensile modulus | | ISO 527-3 | 190 Mpa |
| Tensile modulus | | ISO 527-3 | 190 Mpa |
| tensile strength | | ISO 527-3 | 11.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/A | 98.0 °C |
| melting temperature | | ASTM D3354 | 108 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.