Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTM D792 | 0.830 cm³/g |
| melt mass-flow rate | | ASTM D1238 | 18 g/10 min |
| Shrinkage rate - flow | | 内部方法 | 0.50 到 0.70 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| Water absorption rate | | ASTM D570 | 0.35 % |
| Water absorption rate | | ASTM D570 | 0.58 % |
| Outdoor applicability | | UL 746C | f1 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 70 |
| Rockwell hardness | | ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.586 |
| transmissivity | | ASTM D1003 | 88.0 % |
| Haze ratio | | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength 2 | | ASTM D638 | 62.0 Mpa |
| Tensile strength 2 | | ASTM D638 | 65.0 Mpa |
| | ASTM D638 | 7.0 % |
| | ASTM D638 | 110 % |
| Flexural modulus | | ASTM D790 | 2340 Mpa |
| bending strength | | ASTM D790 | 93.0 Mpa |
| | ASTM D1044 | 10.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap 4 | | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam gap 4 | | ISO 179/1eA | 65 kJ/m² |
| Simple supported beam without notch impact strength 4 | | ISO 179/1eU | 无断裂 |
| Simple supported beam without notch impact strength 4 | | ISO 179/1eU | 无断裂 |
| | ASTM D4812 | 3200 J/m |
| | ISO 180/1U | 无断裂 |
| | ISO 180/1U | 无断裂 |
| Falling hammer impact | | ASTM D3029 | 169 J |
| Tensile impact strength 6 | | ASTM D1822 | 546 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | > 1.0E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 15 KV/mm |
| dielectric constant | | ASTM D150 | 3.17 |
| dielectric constant | | ASTM D150 | 3.17 |
| dielectric constant | | ASTM D150 | 2.96 |
| Dissipation Factor | | ASTM D150 | 9.0E-4 |
| Dissipation Factor | | ASTM D150 | 9.0E-4 |
| Dissipation Factor | | ASTM D150 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 到 60 % |
| Temperature at the rear of the barrel | | | 260 到 280 °C |
| Temperature in the middle of the barrel | | | 270 到 295 °C |
| Temperature at the front of the material cylinder | | | 280 到 305 °C |
| Spray nozzle temperature | | | 275 到 300 °C |
| Processing (melt) temperature | | | 280 到 305 °C |
| Temperature | | | 70 到 95 °C |
| Back pressure | | | 0.300 到 0.700 Mpa |
| screw speed | | | 40 到 70 rpm |
| Exhaust hole depth | | | 0.025 到 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 137 °C |
| Thermal deformation temperature under load | | ASTM D648 | 132 °C |
| vicat | | ASTM D15257 | 154 °C |
| | ASTM E831 | 6.8E-5 cm/cm/°C |
| specific heat | | ASTM C351 | 1260 J/kg/°C |
| thermal conductivity | | ASTM C177 | 0.25 W/m/K |
| RTI Elec | | UL 746 | 100 °C |
| RTI Imp | | UL 746 | 100 °C |
| RTI | | UL 746 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.