'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC EXL1414T SABIC INNOVATIVE US
234
Form：Granules | Grade：Injection grade
Properties:
Low temperature resistanctransparentProcessabilityModerate liquidityDuctilitycopolymer
Typical Applications:
Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesBottle cap
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electrical field | Electronic field | Household appliances | Household appliances | Bottle cap |
| Properties: | Low temperature resistanc | transparent | Processability | Moderate liquidity | Ductility | copolymer |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| transmissivity | 2540 μm | ASTM D1003 | 82.0 | % |
| turbidity | 2540 μm | ASTM D1003 | 3.0 | % |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 | kJ/m² |
| -30°C | ISO 179/1eA | 60 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 | |
| Dart impact | -30°C, Total Energy | ASTM D3763 | 77.0 | J |
| 23°C, Total Energy | ASTM D3763 | 75.0 | J | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.8 mm | UL 94 | HB | |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 850 | °C |
| UL flame retardant rating | 3.0 mm | UL 94 | V-2 | |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 850 | °C |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | Yield, 50.0 mm Span4 | ASTM D790 | 92.0 | Mpa |
| --5,6 | ISO 178 | 88.0 | Mpa | |
| Bending modulus | --5 | ISO 178 | 2120 | Mpa |
| 50.0 mm Span4 | ASTM D790 | 2180 | Mpa | |
| elongation | Break | ISO 527-2/50 | 110 | % |
| Break3 | ASTM D638 | 120 | % | |
| Yield | ISO 527-2/50 | 5.4 | % | |
| Yield3 | ASTM D638 | 5.6 | % | |
| tensile strength | Break | ISO 527-2/50 | 55.0 | Mpa |
| Break3 | ASTM D638 | 59.0 | Mpa | |
| Yield | ISO 527-2/50 | 56.0 | Mpa | |
| Yield3 | ASTM D638 | 57.0 | Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2300 | Mpa |
| --2 | ASTM D638 | 2180 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 to 60 | % | ||
| Temperature at the rear of the barrel | 270 to 295 | °C | ||
| Temperature in the middle of the barrel | 280 to 305 | °C | ||
| drying temperature | 120 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Screw speed | 40 to 70 | rpm | ||
| Exhaust hole depth | 0.025 to 0.076 | mm | ||
| Temperature at the front of the material cylinder | 295 to 315 | °C | ||
| Spray nozzle temperature | 290 to 310 | °C | ||
| Processing (melt) temperature | 295 to 315 | °C | ||
| Mold temperature | 70 to 95 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 120 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9 | ISO 75-2/Af | 116 | °C | |
| Vicat softening temperature | -- | ASTM D152510 | 138 | °C |
| -- | ISO 306/B120 | 139 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 95°C | ASTM E831 | 6.7E-5 | cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 8.0E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 130 | °C | |
| RTI | UL 746 | 130 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | Flow : 3.20 mm | Internal Method | 0.40 - 0.80 | % |
| Melt Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 9.00 | cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.090 | % |
| Saturation, 23°C | ISO 62 | 0.12 | % | |
| Shrinkage rate | Across FlowFlow : 3.20 mm | Internal Method | 0.40 - 0.80 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257 | > 1.0E+15 | ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 | ohms·cm | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | L -Sale | ISO 2039-2 | 87 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.