PC CH8105 1001 CANGZHOU DAHUA

126

Form：Granules | Grade：Injection grade

Properties:

heat-resistingHigh impact resistanceLow viscositytransparentDemolding performance

Typical Applications:

Industrial componentsfilmAutomotive ApplicationsElectronic and electrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Industrial components \| film \| Automotive Applications \| Electronic and electrical components
Properties:	heat-resisting \| High impact resistance \| Low viscosity \| transparent \| Demolding performance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity		ISO 13468	89	%
Cleanliness	2000?	ISO 14782	0.8	%
Refractive index		ISO 489	1.586
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	1.0mm/min	ISO 527	2400	Mpa
tensile strength	Yield50mm/min	ISO 527	60	Mpa
elongation	Yield50mm/min	ISO 527	6	%
elongation	elongation	Break50mm/mi	ISO 527	150	%
bending strength	Yield2.0mm/min	ISO 178	97	Mpa
Bending modulus	2.0mm/min	ISO 178	2410	Mpa
Impact strength of cantilever beam gap	23℃	ISO 180	70	kJ/㎡
Suspended wall beam without notch impact strength	23℃	ISO 180	NB	kJ/㎡
Charpy Notched Impact Strength	23℃	ISO 179	75	kJ/㎡
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	NB	kJ/㎡
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	Annealed0.45MPa	ISO 75	144	°C
Hot deformation temperature	Hot deformation temperature	Unannealed1.8MPa	ISO 75	128	°C
Vicat softening temperature	50℃/hr 50N	ISO 306	149	°C
Glass transition temperature	10℃/min	ISO 11357	149	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.2	g/cm³
Shrinkage rate	Flow2.0mm	ISO 294	0.50-0.70	%
Shrinkage rate	Shrinkage rate	垂直2.0mm	ISO 294	0.50-0.70	%
Water absorption rate	23°C24hr	ISO 62	0.32	%
Water absorption rate	Water absorption rate	23℃ 50RH	ISO 62	0.15	%
melt mass-flow rate	300°C 1.2kg	ISO 1133	10	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	2.0mm	IEC 60093	200000000000000000	Ω.cm
Surface resistivity	2.0mm	IEC 60093	10000000000000000	Ω
Dielectric strength	1.0mm	IEC 60243	34	KV/mm
Dielectric constant	100Hz	IEC 60250	3.1
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3
Dissipation factor	100Hz	IEC 60250	0.001
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.01
Anti leakage trace index		IEC 60112	250	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ISO 2039	120
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Ignition temperature of heating wire	1.5mm	IEC 60695	875	°C
Ignition temperature of heating wire	Ignition temperature of heating wire	3mm	IEC 60695	875	°C
Relative temperature of heating wire	1.5mm	IEC 60695	875	°C
Relative temperature of heating wire	Relative temperature of heating wire	3mm	IEC 60695	960	°C
Extreme Oxygen Index		ISO 4589	27	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.