Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
melt mass-flow rate | | ISO 1133 | 5.0 g/10min |
Shrinkage rate | | ASTM D955 | 0.40-0.70 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 104 |
other | Test Condition | Test Method | Test Result |
---|
characteristic | | | 阻燃性能 |
purpose | | | 汽车配件 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-2 |
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | 5VA |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638/ISO 527 | 27557 kg/cm²(MPa)[Lb/in²] |
tensile strength | | ASTM D638/ISO 527 | 459 kg/cm²(MPa)[Lb/in²] |
Flexural modulus | | ASTM D790/ISO 178 | 23550 kg/cm²(MPa)[Lb/in²] |
bending strength | | ASTM D790/ISO 178 | 693 kg/cm²(MPa)[Lb/in²] |
elongation at break | | ASTM D638/ISO 527 | 5 % |
Tensile modulus | | ISO 527-2/1 | 2700 Mpa |
tensile strength | | ASTM D638 | 45.0 Mpa |
tensile strength | | ISO 527-2/50 | 49.0 Mpa |
elongation | | ASTM D638 | >5.0 % |
Tensile strain | | ISO 527-2/50 | >5.0 % |
Flexural modulus | | ASTM D790 | 2310 Mpa |
bending strength | | ASTM D790 | 68.0 Mpa |
bending strength | | ISO 178 | 70.0 Mpa |
Physical properties | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792/ISO 1183 | 1.15 |
Shrinkage rate | | ASTM D955 | 0.004-0.007 % |
melt mass-flow rate | | ASTM D1238/ISO 1133 | 5 g/10min |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/A | 70.0 °C |
Heat distortion temperature | | ASTM D648 | 76.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.