PA6 B404
0
CompareTechnical Data Sheet
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 3 g/10min | |
| Linear forming shrinkage rate | ASTM D955 | 0.009-0.01 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 110 | |
| density | ASTM D792 | 1.10 g/cm3 |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning residue | 灼烧法 | -- % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strength at break | ASTM D638 | 57 MPa | |
| elongation | Break | ASTM D638 | 75 % |
| bending strength | ASTM D790 | 48 MPa | |
| Flexural modulus | ASTM D790 | 1780 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 30 KJ/m2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D648 | -- ℃ | ||
| melting point | DSC | 220 ℃ | |
| ASTM D648 | 216 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.