SMA XIRAN® SF260
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.35 g/cm³ | |
| melt mass-flow rate | ISO1133 | 20 g/10min | |
| SpiralFlow | 内部方法 | 30.0 cm | |
| Shrinkage rate | 内部方法 | 0.50 % | |
| 内部方法 | 0.20 % | ||
| Water absorption rate | ASTMD570 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 20 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2 | 10000 MPa | |
| Tensile stress | Break | ISO527-2 | 90.0 MPa |
| Tensile strain | Break | ISO527-2 | 1.0 % |
| Flexural modulus | ISO178 | 10500 MPa | |
| Bending stress | ISO178 | 150 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | 130 °C | ||
| vicat | ISO306/B | 135 °C | |
| ASTMD696 | 2.9E-05 cm/cm/°C | ||
| ASTMD696 | 4.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.