Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.65 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20 % |
| Shrinkage rate | | ASTM D955 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 90 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTMD790 | 215 MPa |
| tensile strength | | ASTM D638 | 145 MPa |
| tensile strength | Break | ISO 527-2/5 | 145 MPa |
| Flexural modulus | | ASTM D790 | 10200 MPa |
| Flexural modulus | | ISO 178 | 10000 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 29 kV/mm |
| dielectric constant | | ASTM D150 | 3.30 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 228 °C |
| Heat distortion temperature | | ISO 75-2/A | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.