PC 121R-111 SABIC INNOVATIVE SPAIN

Form：Granules | Grade：Injection grade

Properties:

Low viscositytransparent

Typical Applications:

building materialsProfile

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	building materials \| Profile
Properties:	Low viscosity \| transparent

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ISO 489	1.586
transmissivity	2540 μm	ASTM D1003	88.0 to 90.0	%
turbidity	2540 μm	ASTM D1003	< 0.80	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	65	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.70 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	1.0 mm	IEC 60695-2-12	850	°C
Extreme Oxygen Index		ISO 4589-2	25	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2350	Mpa
tensile strength	Yield	ISO 527-2/50	63.0	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	65.0	Mpa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	100	%
Bending modulus		ISO 178	2300	Mpa
bending strength		ISO 178	90.0	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	10.0	mg
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			260 to 280	°C
Temperature in the middle of the barrel			270 to 290	°C
Temperature at the front of the material cylinder			280 to 300	°C
Spray nozzle temperature			270 to 290	°C
Processing (melt) temperature			280 to 300	°C
Mold temperature			80 to 100	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	133	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	122	°C
Vicat softening temperature	--	ISO 306/B50	140	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	141	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	23 to 80°C，Across Flow	ISO 11359-2	7.0E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	125	°C
RTI		UL 746	125	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	21.0	cm3/10min
Shrinkage rate	Flow	Internal Method	0.50 - 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35	KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	27	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Relative permittivity	50 Hz	IEC 60250	2.70
	Relative permittivity	60 Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.70
Dissipation factor	50 Hz	IEC 60250	1.0E-3
	Dissipation factor	60 Hz	IEC 60250	1.0E-3
	Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.010
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 358/30	ISO 2039-1	95.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.