Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183/B | 1.05 g/cm³ |
| density | | ISO11832 | 1050 kg/m³ |
| Apparent density | | ISO60 | 0.65 g/cm³ |
| melt mass-flow rate | | ISO1133 | 4.5 g/10min |
| Melt volume flow rate | | ISO1133 | 4.70 cm³/10min |
| Melt volume-flowrate | | ISO11332 | 4.00 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.40to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Normal thickness for combustion performance | | ISO12102 | HB |
| Carbon Emissions | | VDA277 | 20.0 µg/g |
| burning rate | | ISO3795 | 40 mm/min |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 1900 MPa |
| bending strength | | ISO178 | 58.0 MPa |
| Tensile modulus | | ISO527-2 | 1820 MPa |
| Tensile modulus | | ISO527-22 | 1900 MPa |
| Tensile stress | | ISO527-2/50 | 37.0 MPa |
| Tensile stress | | ISO527-2/100 | 39.0 MPa |
| Tensile stress | Yield | ISO527-22 | 35.0 MPa |
| Tensile strain | | ISO527-2/50 | 2.6 % |
| Tensile strain | | ISO527-2/100 | 2.8 % |
| Tensile strain | Yield | ISO527-22 | 2.5 % |
| Nominal strainatbreak | | ISO527-22 | 45 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/2C | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 18 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 37 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/2C | 22 kJ/m² |
| CharpyNotchedImpactStrength | | ISO179/1eA2 | 38.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA2 | 16.0 kJ/m² |
| Charpy impact strength | | ISO179/1eU2 | NoBreak |
| CharpyImpactStrength | | ISO179/1eU2 | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/A | 17 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 42 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC600932 | >1.0E+13 ohms·m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 97.0 °C |
| | ISO75-22 | 97.0 °C |
| vicat | | ISO306/B50 | 97.0 °C |
| vicat | | ISO3062 | 97.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.