Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 1.27 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 105 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | DIN53491 | 1.5700 |
| transmissivity | | DIN5036 | 88.0 % |
| Haze ratio | | ASTMD1003 | <1.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | >280 °C |
| SheetTemperature-Forming | | | 120到160 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | DIN53455 | 2200 MPa |
| Tensile stress | | DIN53455 | 50.0 MPa |
| Tensile strain | Break | DIN53455 | 54 % |
| Flexural modulus | | DIN53452 | 2080 MPa |
| Bending stress | | DIN53452 | 70.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | DIN53453 | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | DIN53453 | 无断裂 |
| Impact strength of cantilever beam gap | | ISO180 | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | >1.0E+16 ohms |
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 16 kV/mm |
| dielectric constant | | IEC60250 | 2.60 |
| Dissipation Factor | | IEC60250 | 0.010 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | DIN53461 | 68到72 °C |
| maximum service temperature | | | 70 °C |
| | DIN53752 | 6.8E-05 cm/cm/°C |
| specific heat | | ASTMD2766 | 1100 J/kg/°C |
| thermal conductivity | | DIN52612 | 0.20 W/m/K |
| vicat | | DIN534602 | 82.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.