Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 11 g/10 min |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 32.0 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO 2039-1 | 103 Mpa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2300 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2300 Mpa |
| tensile strength | | ASTM D638 | 37.9 Mpa |
| tensile strength | | ISO 527-2/50 | 41.0 Mpa |
| Flexural modulus | | ASTM D790 | 2200 Mpa |
| Flexural modulus | | ISO 178 | 2200 Mpa |
| Bending stress 6 | | ISO 178 | 65.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+16 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+18 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 KV/mm |
| | IEC 60250 | 2.90 |
| | IEC 60250 | 2.90 |
| Dissipation Factor | | IEC 60250 | 7.3E-3 |
| Dissipation Factor | | IEC 60250 | 9.0E-3 |
| injection | Test Condition | Test Method | Test Result |
|---|
| Processing (melt) temperature | | | 240 °C |
| Temperature | | | 80 °C |
| Injection Velocity | | ISO 294 | 14 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 97.0 °C |
| | ISO 75-2/A | 92.0 °C |
| vicat | | ASTM D15257, ISO 306/B507 | 95.0 °C |
| vicat | | ISO 306/B120 | 97.0 °C |
| | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| | ISO 11359-2 | 1.0E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.