PPO GTX974 SABIC INNOVATIVE US

124

Form：Granules | Grade：Injection grade

Properties:

Conductive

Typical Applications:

Automotive interior partsHousehold appliances

Supplier(4)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts \| Household appliances
Properties:	Conductive

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--3	ASTM D638	2300	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400	Mpa
tensile strength	Yield4	ASTM D638	65.0	Mpa
	tensile strength	Yield	ISO 527-2/50	65.0	Mpa
		tensile strength	Break4	ASTM D638	55.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0	Mpa
elongation	Yield4	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	4.5	%
		elongation	Break4	ASTM D638	60	%
		elongation	elongation	Break	ISO 527-2/50	25	%
Bending modulus	50.0mmSpan5	ASTM D790	2350	Mpa
Bending modulus	Bending modulus	--6	ISO 178	2200	Mpa
bending strength	--6,7	ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	95.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.23	W/m/K
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	190	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan10	ISO 75-2/Be	190	°C
Vicat softening temperature	--	ASTM D-596	205	°C
	Vicat softening temperature	--	ISO 306/A50	250	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	200	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:3.20mm	Internal Method	1.1-1.4	%
Water absorption rate	Saturation,23°C	ISO 62	3.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
melt mass-flow rate	280°C/5.0kg	ASTM D1238	13	g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	13.0	cm3/10min
Shrinkage rate	MD2	Internal Method	1.6-2.0	%
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	1.4-1.7	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	85.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPO GTX974 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index