Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.67 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.45 % |
| Water absorption rate | | ISO 62 | 0.18 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10,-20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 14000 MPa |
| tensile strength | Break | ISO 527-2 | 150 MPa |
| Tensile strain | Break | ISO 527-2 | 1.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 14.0 |
| Volume resistivity | | IEC 60093 | 3E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 1.1 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 235 °C |
| melting temperature | | ISO 11357-3 | 255 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4E-05 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.80 W/m/K |
| thermal conductivity | | ASTME1461 | 1.7 W/m/K |
| Heat distortion temperature | | ISO 75-2/B | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.