POM Copolymer LUVOCOM® 80/TF/18/SI/2-3

Usages:
Gears
bearings
textile applications
engineering accessories
automotive applications
business equipment
cams
Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO1183	1.49 g/cm³
melt mass-flow rate	ISO1133	11 g/10min
Shrinkage rate	DIN16901	1.8到2.5 %
Water absorption rate		<0.10 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2	2500 MPa
Tensile stress	Break	ISO527-2	45.0 MPa
Tensile strain	Yield	ISO527-2	20 %
Flexural modulus		ISO178	2000 MPa
Bending stress		ISO178	60.0 MPa
Bending Strain		ISO178	25 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch		ISO179/1fU	42 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1eU	60 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
insulation resistance		IEC60167	>1.0E+12 ohms

Thermal performance	Test Method	Test Result
Heat distortion temperature	ISO75-2/A	95.0 °C
Continuous use temperature	UL746B	100 °C
Maximum operating temperature - SharrTerm		120 °C
vicat	ISO306/A	160 °C
	DIN53752	9E-05 cm/cm/°C
thermal conductivity	DIN52612	0.20 W/m/K

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.