'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC D251-701 SABIC INNOVATIVE NANSHA
115
Form：Granules | Grade：Injection grade
Properties:
Non chloro non bromine flGlass fiber reinforced
Typical Applications:
Electronic and Electrical ApplicationsPlastic bag
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electronic and Electrical Applications | Plastic bag |
| Properties: | Non chloro non bromine fl | Glass fiber reinforced |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 22.0 | J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 720 | J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 51 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.300mm | UL 94 | V-2 | |
| 0.600mm | UL 94 | V-0 | ||
| 0.500mm | UL 94 | V-1 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| --5 | ISO 178 | 6240 | Mpa | |
| --6 | ISO 178 | 165 | Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 167 | Mpa | |
| --1 | ASTM D638 | 6680 | Mpa | |
| crack | ASTM D638 | 110 | Mpa | |
| ISO 527-2/5 | 112 | Mpa | ||
| ASTM D638 | 2.7 | % | ||
| ISO 527-2/5 | 2.6 | % | ||
| 50.0mm span | ASTM D790 | 6150 | Mpa | |
| --5 | ISO 178 | 6240 | Mpa | |
| --6 | ISO 178 | 165 | Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 167 | Mpa | |
| --1 | ASTM D638 | 6680 | Mpa | |
| crack | ASTM D638 | 110 | Mpa | |
| ISO 527-2/5 | 112 | Mpa | ||
| ASTM D638 | 2.7 | % | ||
| ISO 527-2/5 | 2.6 | % | ||
| 50.0mm span | ASTM D790 | 6150 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTM D648 | 121 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 116 | °C | |
| Linear coefficient of thermal expansion | MD:23to80°C | ISO 11359-2 | 2.6E-05 | cm/cm/°C |
| TD:23to80°C | ISO 11359-2 | 7.3E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.030 | % |
| Saturation,23°C | ISO 62 | 0.070 | % | |
| Shrinkage rate | TD:24hr | ASTM D955 | 0.20-0.40 | % |
| MD:24hr | ASTM D955 | 0.20-0.40 | % | |
| Melt Volume Flow Rate (MVR) | 300°C/2.16kg | ISO 1133 | 29.0 | cm3/10min |
| 300°C/1.2kg | ISO 1133 | 15.0 | cm3/10min | |
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 33 | g/10min |
| 300°C/1.2kg | ASTM D1238 | 17 | g/10min | |
| density | ASTM D792 | 1.35 | g/cm³ | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 20.0GHz | Internal Method | 6.5E-03 | |
| 10.0GHz | Internal Method | 6.7E-03 | ||
| 5.00GHz | Internal Method | 6.4E-03 | ||
| 1.90GHz | Internal Method | 6.3E-03 | ||
| 1.10GHz | Internal Method | 6.3E-03 | ||
| Dielectric constant | 20.0GHz | Internal Method | 3.20 | |
| 10.0GHz | Internal Method | 3.20 | ||
| 5.00GHz | Internal Method | 3.20 | ||
| 1.90GHz | Internal Method | 3.20 | ||
| 1.10GHz | Internal Method | 3.20 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.