Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 16 g/10min |
| Shrinkage rate | | ISO 294-4 | 0.40to0.70 % |
| VOCContent-Condition | | VDA277 | <18.0 µgC/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| atomization | | DIN 75201 | <2.0 mg |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Ethylbenzene | | VDA277 | <8.00 µg/g |
| Odor | | VDA270 | Grade2 |
| Odor | | VDA270 | Grade3 |
| Odor | | VDA270 | Grade3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 65.0 MPa |
| Poisson's ratio | | ISO 527 | 0.38 |
| tensile strength | | ISO 527-2/50 | 45.0 MPa |
| Tensile strain | Break | ISO 527-2/50 | 30 % |
| Flexural modulus | | ISO 178 | 2300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 18 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 95.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 82.0 °C |
| vicat | | ISO 306/B50 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare