PBT B4406G3 Q117 BASF GERMANY

100

Form：Granules | Grade：Enhanced level

Properties:

High mobilityFlame retardantGlass fiber reinforcedFiller: Glass fiber reinf30%Filler by weight

Typical Applications:

Thin walled componentsswitchShellElectrical componentsLaptop case

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Thin walled components \| switch \| Shell \| Electrical components \| Laptop case
Properties:	High mobility \| Flame retardant \| Glass fiber reinforced \| Filler: Glass fiber reinf \| 30% \| Filler by weight

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	6.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	6.5	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	32	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	6.1	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	6.1	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
		UL flame retardant rating	0.75mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	0.40mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ISO 178	6050	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.7	%
tensile strength	Break,23°C	ISO 527-2	110	Mpa
Tensile modulus	23°C	ISO 527-2	6500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str	3.0mm	UL 746	130	°C
	RTI Str	1.5mm	UL 746	130	°C
		RTI Str	0.75mm	UL 746	125	°C
		RTI Str	RTI Str	0.40mm	UL 746	75.0	°C
RTI Imp	3.0mm	UL 746	130	°C
	RTI Imp	1.5mm	UL 746	130	°C
		RTI Imp	0.75mm	UL 746	130	°C
		RTI Imp	RTI Imp	0.40mm	UL 746	75.0	°C
RTI Elec	3.0mm	UL 746	140	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	217	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	195	°C
Melting temperature		ISO 3146	223	°C
RTI Elec	0.40mm	UL 746	75.0	°C
	RTI Elec	0.75mm	UL 746	140	°C
	RTI Elec	RTI Elec	1.5mm	UL 746	140	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Viscosity value	降低的粘度	ISO 1628	116.0	ml/g
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.40	%
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	13.0	cm3/10min
density		ISO 1183	1.55	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+13	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top