Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 7.0 g/10min |
| Shrinkage rate | | ISO 2577 | 0.40to0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | 67 mm/min |
| UL flame retardant rating | | 内部方法 | HB |
| UL flame retardant rating | | 内部方法 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 50.0 MPa |
| tensile strength | Break | ISO 527-2 | 40.0 MPa |
| Tensile strain | Break | ISO 527-2 | 20 % |
| Flexural modulus | | ISO 178 | 2700 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 26 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 108 °C |
| vicat | | ISO 306/A50 | 118 °C |
| vicat | | ISO 306/B50 | 111 °C |
| vicat | | | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.