Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | <2.0 % |
| PostShrinkage | | ISO2577 | 1.0到1.5 % |
| density | | ISO1183 | 1.50到1.70 g/cm³ |
| Apparent density | | ISO60 | 0.55到0.75 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.90到1.3 % |
| Shrinkage rate | | ISO2577 | 0.60到1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 900 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >20.0 MPa |
| CompressionMoldingTemperature | | | 160到180 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 7.0到11 kJ/m² |
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 1.2到1.8 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 1.4到2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 5.0到9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO527-2 | 5000到8000 MPa |
| Tensile modulus | Injection | ISO527-2 | 5000到8000 MPa |
| Tensile stress | | ISO527-2 | 45.0到65.0 MPa |
| Tensile stress | Injection | ISO527-2 | 60.0到85.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 7000到9000 MPa |
| Flexural modulus | Injection | ISO178 | 7000到9000 MPa |
| Bending stress | Compression Molded | ISO178 | 80.0到110 MPa |
| Bending stress | Injection | ISO178 | 100到130 MPa |
| compression stress | | ISO604 | 200到250 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC60093 | 1.0E+11到1.0E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 15到20 kV/mm |
| | IEC60250 | 11.016.0 |
| | IEC60250 | 7.009.00 |
| Dissipation Factor | | IEC60250 | 0.30到0.50 |
| Dissipation Factor | | IEC60250 | 0.030到0.050 |
| arc resistance | | ASTMD495 | PLC 5 |
| CTI | | IEC60112 | >250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 155到180 °C |
| | ISO75-2/C | 110到130 °C |
| | ISO11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.50到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 160 °C |
| maximum service temperature | | IEC60216 | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.