Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 260°C/2.16kg | ISO1133 | 44 | g/10min |
| Melt Volume-Flow Rate (MVR) | 260°C/2.16kg | ISO1133 | 48.0 | cm3/10min |
| Shrinkage rate | | 内部方法 | 0.10到0.50 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.010 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/1A/1 | 3200 | Mpa |
| tensile strength | 屈服 | ISO527-2/1A/50 | 46.0 | Mpa |
| elongation | 屈服 | ISO527-2/1A/50 | 1.7 | % |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 13 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 127 | °C |
| Glass transition temperature | | ISO11357-2 | 134 | °C |
| vicat softening point | | ISO306/B50 | 135 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | >1.0E+16 | ohms·cm |
| Relative permittivity | 1kHz | IEC60250 | 2.35 | |
| Relative permittivity | 10kHz | IEC60250 | 2.35 | |
| Leakage Trace Index | | IEC60112 | >600 | V |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ISO489 | 1.530 | |
| Light transmittance | | ISO13468-2 | 91.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.