Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238,ISO1133 | 9.0 g/10min |
| Content of comonomer 3 | | 内部方法 | 6.5 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Monomer content | | % | Internal Method |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Sealing starting temperature | | ℃ | Internal Method 92.8 |
| Water vapor transmission rate | | g·mm/m | DIN 53122/2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile yield strength | | ASTM D-638 | 7.89 MPa |
| tensile yield strength | | ISO 527-2 | 7.89 MPa |
| tensile strength | | ASTMD638,ISO527-2 | 7.89 Mpa |
| tensile strength | | ASTMD638,ISO527-2 | 17.2 Mpa |
| elongation | | ASTMD638,ISO527-2 | 630 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Initial sealing temperature 4 | | 内部方法 | 92.8 °C |
| Water vapor permeability | | DIN53122/2 | 0.40 g·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D-1525 | 83.9 ℃ |
| vicat | | ISO 306 | 83.9 ℃ |
| melting temperature | | ℃ | Internal Method 101 |
| vicat | | ASTMD1525,ISO306 | 83.9 °C |
| Melting temperature (DSC) | | 内部方法 | 101 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.