PA66 133 GHU BK155
0
- Properties:Glass fiber reinforced material33%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.4 g/cm3 | |
| Shrinkage rate | ISO 2577 | 0.15-0.4 % | |
| Water absorption rate | ISO 62 | 0.9 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ISO 527-2 | 160 MPa |
| Tensile strain | Yield | ISO 527-2 | 2.5 % |
| Break | ISO 527-2 | 2.5 % | |
| Flexural modulus | ISO 178 | 8600 MPa | |
| bending strength | ISO 178 | 260 MPa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 7.5 kJ/m2 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | PLC 0 | ||
| Volume resistivity | ISO 1325 | 1E+14 ohm·cm | |
| dielectric strength | ASTM D149 | 16 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 249 ℃ | |
| melting temperature | ASTM D789 | 257 ℃ | |
| UL flame retardant rating | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| Linear coefficient of thermal expansion | ASTM D696 | 0.00005 cm/cm/℃ | |
| FMVSS combustion rate | FMVSS 302 | PASSED |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.