Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.4-0.6 % |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 标准级 |
| purpose | | | 高冲击 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D-1238 | 12 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790/ISO 178 | 2.4 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 70 kg/cm²(MPa)[Lb/in²] |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 225 kg·cm/cm(J/M)ft·lb/in |
| tensile strength | | ASTM D-638 | 47 Mpa |
| Impact strength of cantilever beam gap | | ASTM D-256 | 225 J/m |
| Flexural modulus | | ASTM D-790 | 2500 Mpa |
| bending strength | | ASTM D-790 | 75 Mpa |
| Shore hardness | | ASTM D-785 | 117 |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Surface intrinsic resistance | | JIS K8911 | >1010 Ω |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.04 |
| Shrinkage rate | | ASTM D955 | 0.4-0.6 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648/ISO 75 | 89 ℃（℉） |
| Heat distortion temperature | | ASTM D-648 | 90 °C |
| vicat | | ASTM D-1525 | 102 °C |
| combustibility | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.