Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.70到0.85 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.30到0.50 % |
| Water absorption rate | | ISO62 | <0.30 % |
| density | | ISO1183 | 2.00到2.20 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC60695-2-13 | 930 °C |
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO527-2 | 9000到11000 MPa |
| Tensile stress | | ISO527-2 | 50.0到70.0 MPa |
| Flexural modulus | Injection | ISO178 | 16000到18000 MPa |
| Bending stress | Injection | ISO178 | 130到150 MPa |
| compression stress | | ISO604 | 120到170 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 4.0到4.5 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 13到16 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+13到1.0E+14 ohms |
| Volume resistivity | | IEC60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 25到35 kV/mm |
| | IEC60250 | 6.005.00 |
| | IEC60250 | 5.004.00 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTME1461 | 0.90到1.1 W/m/K |
| | ISO11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.