POM Copolymer LUVOCOM® 80/TF/18/SI/2/BK

Usages:
Applications in the fields of bearings
automobiles
engineering accessories
rollers
business equipment
gears
textile applications
Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ISO 1183	1.49 g/cm³
Shrinkage rate	DIN 16901	1.8to2.5 %
Water absorption rate		<0.10 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2	40.0 MPa
Tensile strain	Yield	ISO 527-2	15 %
Flexural modulus		ISO 178	1800 MPa
bending strength		ISO 178	60.0 MPa
Bending Strain		ISO 178	18 %
Tensile modulus		ISO 527-2	2000 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1fU	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1fU	60 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
insulation resistance		IEC 60167	>1.0E+12 ohms

Thermal performance	Test Method	Test Result
vicat	ISO 306/A	160 °C
Linear coefficient of thermal expansion	DIN 53752	9E-05 cm/cm/°C
thermal conductivity	DIN 52612	0.20 W/m/K
Heat distortion temperature	ISO 75-2/A	95.0 °C
Continuous use temperature	UL 746B	100 °C
maximum service temperature		120 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.