PA66 CM3006 TORAY JAPAN

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityFlame retardant

Typical Applications:

Automotive sectorElectrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Electrical components
Properties:	Thermal stability \| Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-40°C		无断裂	--
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C		无断裂	--
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.79mm		V-2	--
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃，24hr	ASTM D-570	无水｜1.2	%
Water absorption rate	Water absorption rate	23℃，24hr	ASTM D-570	3.5%水｜-	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Shear strength	23℃	ASTM D-732	3.5%水｜770	kg/cm2
bending strength	80℃	ASTM D-790	无水｜640	kg/cm2
bending strength	bending strength	80℃	ASTM D-790	3.5%水｜400	kg/cm2
Bending modulus	80℃	ASTM D-790	无水｜9000	kg/cm2
Bending modulus	Bending modulus	80℃	ASTM D-790	3.5%水｜5000	kg/cm2
Rockwell hardness	23℃	ASTM D-785	无水｜119	R-标度
Rockwell hardness	Rockwell hardness	23℃	ASTM D-785	3.5%水｜100	R-标度
Bending modulus	23℃	ASTM D-790	无水｜29000	kg/cm2
Elongation at Break	23℃	ASTM D-638	无水｜90	%
Elongation at Break	Elongation at Break	23℃	ASTM D-638	3.5%水｜< 200	%
Impact strength of cantilever beam gap	-40℃，VNotched1/2	ASTM D-256	无水｜3.5	kg·cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40℃，VNotched1/2	ASTM D-256	3.5%水｜-	kg·cm/cm
Bending modulus	-40℃	ASTM D-790	无水｜44000	kg/cm2
Bending modulus	Bending modulus	-40℃	ASTM D-790	3.5%水｜42000	kg/cm2
Rockwell hardness	23℃	ASTM D-785	无水｜97	M-标度
Rockwell hardness	Rockwell hardness	23℃	ASTM D-785	3.5%水｜-	M-标度
Shear strength	23℃	ASTM D-732	无水｜790	kg/cm2
bending strength	-40℃	ASTM D-790	3.5%水｜1300	kg/cm2
Impact strength of cantilever beam gap	23℃，Unnotched1/8		无水｜无断裂	kg·cm/cm2
tensile strength	23℃，Yield	ASTM D-638	3.5%水｜530	kg/cm2
compressive strength	23℃	ASTM D-695	无水｜910	kg/cm2
compressive strength	compressive strength	23℃	ASTM D-695	3.5%水｜-	kg/cm2
bending strength	23℃	ASTM D-790	无水｜1150	kg/cm2
bending strength	bending strength	23℃	ASTM D-790	3.5%水｜650	kg/cm2
tensile strength	80℃，Yield	ASTM D-638	无水｜430	kg/cm2
tensile strength	tensile strength	80℃，Yield	ASTM D-638	3.5%水｜400	kg/cm2
Bending modulus	23℃	ASTM D-790	3.5%水｜14000	kg/cm2
tensile strength	23℃，Yield	ASTM D-638	无水｜800	kg/cm2
Impact strength of cantilever beam gap	23℃，Unnotched1/8		3.5%水｜-	kg·cm/cm2
	Impact strength of cantilever beam gap	23℃，VNotched1/2	ASTM D-256	无水｜5	kg·cm/cm
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃，VNotched1/2	ASTM D-256	3.5%水｜28	kg·cm/cm
tensile strength	-40℃，Yield	ASTM D-638	无水｜1150	kg/cm2
tensile strength	tensile strength	-40℃，Yield	ASTM D-638	3.5%水｜1100	kg/cm2
bending strength	-40℃	ASTM D-790	无水｜1450	kg/cm2
	bending strength	-40°C		140	MPa
		bending strength	23°C	MPa	115	65.0
		bending strength	bending strength	80°C	MPa	65.0	40.0
Compressive stress	23°C	MPa	90.0	--
shear strength	23°C	MPa	80.0	75.0
Taber abraser	1000Cycles	mg	8.00	--
Friction coefficient vs. Metal			0.15to0.20	--
tensile strength	-40°C		115	MPa
	tensile strength	23°C	MPa	80.0	50.0
	tensile strength	tensile strength	80°C	MPa	40.0	40.0
Tensile strain	Yield,23°C	%	1.5	--
Tensile strain	Tensile strain	Break,23°C	%	25
Bending modulus	-40°C	MPa	4300	4100
	Bending modulus	23°C	MPa	2900	1400
	Bending modulus	Bending modulus	80°C	MPa	900	500
Charpy Notched Impact Strength		ASTM D256/ISO 179	50	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	2.8	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	4.6kg/cm2	ASTM D-648	无水｜220	°C
Hot deformation temperature	Hot deformation temperature	4.6kg/cm2	ASTM D-648	3.5%水｜-	°C
Melting temperature		差示扫描测热计DSC	265	°C
specific heat			无水｜0.4	Cal/g·℃
specific heat	specific heat			3.5%水｜-	Cal/g·℃
Linear coefficient of thermal expansion		ASTM D-696	无水｜9-10	×10-5cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D-696	3.5%水｜-	×10-5cm/cm/℃
UL-94 flame retardant grade	1/32"	UL 94	无水｜V-2
UL-94 flame retardant grade	UL-94 flame retardant grade	1/32"	UL 94	3.5%水｜-
thermal conductivity			无水｜0.21	Kcal/m·hr·℃
thermal conductivity	thermal conductivity			3.5%水｜-	Kcal/m·hr·℃
Hot deformation temperature	0.45MPa,Unannealed	°C	220	--
Melting temperature		°C	265	--
Linear coefficient of thermal expansion	MD	cm/cm/°C	9.0E-5到1.0E-4	--
specific heat		J/kg/°C	2100	--
thermal conductivity		W/m/K	0.32	--
Combustibility (rate)		UL 94	V-2
Hot deformation temperature	HDT	ASTM D648/ISO 75	220(0.46MPa)	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.32	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000g,CS-17	ASTM D-1044	3.5%水｜-	mg/1000次
Taber abraser	Taber abraser	1000g,CS-17	ASTM D-1044	无水｜8	mg/1000次
Shrinkage rate	MD：1.00mm3	%	0.80-1.5	--
Shrinkage rate	Shrinkage rate	MD：3.00mm4	%	1.5-2.2	--
Water absorption rate	23°C,24hr	%	1.2	--
Water absorption rate	Water absorption rate	Saturation,23°C	%	8.0	--
density		ASTM D792/ISO 1183	1.14
Water absorption rate		ASTM D570/ISO 62	1.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D-257	3.5%水｜1012-1013	Ω.cm
Dissipation factor	50Hz	ASTM D-150	无水｜0.06
Dissipation factor	Dissipation factor	50Hz	ASTM D-150	3.5%水｜-
Compared to the Leakage Traceability Index (CTI)		UL 746	无水｜-	V
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)		UL 746	3.5%水｜530	V
Dielectric constant	50Hz	ASTM D-150	无水｜1.6
Dielectric constant	Dielectric constant	50Hz	ASTM D-150	3.5%水｜-
Volume resistivity		ASTM D-257	无水｜1014-1015	Ω.cm
Volume resistivity	Volume resistivity		ohms·cm	1.0E+13-1.0E+14	1.0E+12到1.0E+13
Dielectric constant	23°C,50Hz		1.60	--
Dissipation factor	23°C,50Hz		0.060	--
Compared to the anti leakage trace index	CTI	V		--
Dielectric constant		ASTM D150/IEC 60250	3.3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C		119
Rockwell hardness	Rockwell hardness	R-Sale,80°C		97	--

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.