PC/ABS NE-1030 W95850 Samsung Cheil South Korea

Form：Granules | Grade：Flame retardant grade

Properties:

Flame retardant

Typical Applications:

Tool handleTV

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Tool handle \| TV
Properties:	Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	17	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	16	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	87.0	Mpa
bending strength	bending strength		ISO 178	90.0	Mpa
Bending modulus		ISO 178	2500	Mpa
Bending modulus	Bending modulus		ASTM D790	2500	Mpa
Tensile strain	Break	ISO 527-2/50	35	%
elongation	Break	ASTM D638	59	%
tensile strength	Break	ISO 527-2/50	46.0	Mpa
	tensile strength	Break	ASTM D638	54.0	Mpa
		tensile strength	Yield	ISO 527-2/50	60.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	63.0	Mpa
Tensile modulus		ISO 527-2/50	2500	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2600	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	95.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	93.0	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	85.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	77.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	83.0	°C
			Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	93.0	°C
			Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD：3.20mm	ASTM D955	0.33-0.40	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.32-0.39	%
melt mass-flow rate	220°C/10.0kg	ISO 1133	53	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	53	g/10min
Shrinkage rate	MD:3.20mm	ISO 2577	0.32-0.39	%
Shrinkage rate	Shrinkage rate	TD:3.20mm	ISO 2577	0.33-0.40	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.